Note ABES Nouveaux matériaux à base de polyoxotitanates (POTs) dopé ou à base de complexe salicylate de titane (IV) et d'argent (I) New materials based on polyoxotitanates (POTs) or based on titanium (IV) and silver (I) salicylate complex Polyoxotitanate (POT) POT dopé Photoluminescence Propriétés antimicrobiennes Polyoxotitanate (POT) Doped POT Photoluminescence Antimicrobial propertie 541 Photoluminescence Récepteurs nicotiniques Neurotransmetteurs -- Récepteurs Ces dernières années, le dioxyde de titane a attiré beaucoup d'attention en tant que matériau hautement stable avec une large gamme d'applications allant du pigment blanc à des applications en tant que semi-conducteur ou dispositifs photoniques de pointe. En utilisant des approches synthétiques récemment développées, la synthèse de molécules cages de type polyoxotitanate (POT, [TixOy(OR)z]) atomiquement bien définies peut être menée. Les POTs peuvent être considérés comme des modèles solubles du TiO2. Des cages dopées avec un métal M (M-POT) présentant de nouvelles propriétés peuvent être aussi préparées.Deux nouvelles cages dopées au cérium ont été synthétisées par une réaction solvothermique. Les cages [Ti28O38(OEt)38CeCl](EtOH)1,4 et [Ti8O7(OEt)21Ce](EtOH) ayant des solubilités différentes, elles vont pouvoir être séparées et caractérisées par RMN du 1H et diffraction des rayons X. Des cages POTs dopées au Fe : [Ti4(OEt)15O(FeCl)] et [FeTi14(OEt)28O14(OH)2] ont été également synthétisés.Puis après hydrolyse avec ou sans calcination, les matériaux à base de Ce ou Fe et TiO2 peuvent être obtenus. Des émulsions de ses matériaux et avec le polymère PVDC dopées au cérium ou au fer ont ensuite été déposées sur une surface de PVC. Les performances d'absorption UV et de barrière à l'eau augmentent progressivement avec l'augmentation de la quantité de matériaux déposés. Les résultats sont intéressants pour l’emploi de ces matériaux en surface d’’emballage de tablettes de médicaments, ce qui permettra d’augmenter la date de péremption de ceux-ci.La cage Eu-POT dopée avec l’Eu (III) : Ti2O(OEt)8EuIIICl(EtOH)]2 a été synthétisé, puis après hydrolyse et calcination, les propriétés de photoluminescence du matériau obtenu ont été étudiées.Enfin, un complexe AgITiIV(SC)2(HSC)(CH3CN) (SC2- = l'acide salicylique) a été préparé. Après hydrolyse et calcination, les propriétés antimicrobiennes des matériaux fabriqués ont été testé vis-à-vis avec succès du S. aureus ou de E. Colis. In recent years, titanium dioxide has attracted much attention as a highly stable material with a wide range of applications from white pigment to its applications as a semiconductor or advanced photonic devices. Using recently developed synthetic approaches, the synthesis of atomically well-defined polyoxotitanate (POT, [TixOy(OR)z]) cage molecules can be determined. POTs may be preferred as soluble models of TiO2. Cages doped with a metal M (M-POT) presenting new properties can also be prepared.Two new cages doped with cerium were synthesized by a solvothermal reaction. The cages [Ti28O38(OEt)38CeCl](EtOH)1.4 and [Ti8O7(OEt)21Ce](EtOH) having different solubilities, they will be able to be separated and characterized by 1H NMR and X-ray diffraction. The Fe-doped POTs: [Ti4(OEt)15O(FeCl)] and [FeTi14(OEt)28O14(OH)2] were also synthesized. Then after hydrolysis with or without calcination, materials based on Ce or Fe and TiO2 can be obtained. Emulsions of its materials and with the cerium-doped PVDC polymer were then deposited on a PVC surface. UV absorption and water barrier performance gradually increases with increasing amount of deposited materials. The results are interesting for the use of these materials on the packaging surface of drug tablets, which will increase their expiry date. The Eu-POT cage doped with the Eu(III): Ti2O(OEt)8EuIIICl(EtOH)]2 was also synthesized, then after hydrolysis and calcination, the photoluminescence properties of the obtained material were studied.Finally, an AgITiIV(SC)2(HSC)(CH3CN) complex (SC2- = salicylate) was prepared. After hydrolysis and calcination, the anti-microbial properties of the materials were successfully tested against S. aureus or E. Colis. Electronic Thesis or Dissertation Text en PDF 60015926 application/pdf 65421650 https://publication-theses.unistra.fr/public/theses_doctorat/These_confidentielle.pdf http://www.theses.fr/2023STRAF062/abes Cai Zhiwei 1990-10-08 FR 276453670 203187707DG 21927256 4200003 https://theses.fr/2023STRAF062 2023STRAF062 https://doi.org/10.70675/a9847d84zef90z4085z98fbzafd62572d00c 2023-12-18 Chimie Strasbourg 131056549 Doctorat Docteur es non oui Ruhlmann Laurent MADS_DIRECTEUR_DE_THESE_1 12334283X Boudon Corinne MADS_DIRECTEUR_DE_THESE_2 058611126 Floquet Sébastien MADS_RAPPORTEUR_1 166429945 Schaming Delphine MADS_RAPPORTEUR_2 146470664 École doctorale des Sciences chimiques (Strasbourg ; 1995-....) MADS_ECOLE_DOCTORALE_1 222 156504081 Institut de chimie (Strasbourg ; 2005-....) MADS_PARTENAIRE_DE_RECHERCHE_1 93761 15677738X ddc:540 Ruhlmann Laurent Boudon Corinne Floquet Sébastien Schaming Delphine École doctorale des Sciences chimiques (Strasbourg ; 1995-....) Institut de chimie (Strasbourg ; 2005-....) PDF 60015926 confidentialité 2023-12-18 2026-12-18 confidentialité 2023-12-18 2026-12-18 confidentialité 2023-12-18 2026-12-18 confidentialité 2023-12-18 2026-12-18